Stainless Steel Cut Wires
Stainless Steel Cut Wire is widely
used for shot peening to give compressive residual stress in the
surface layer of components for fatigue life enhancement and
suppression of stress corrosion cracking as well as cleaning and
polishing of the surface of metal parts, deburring of die cast
parts, is of reusable and recyclable, the working life is 1000 times
of glass bead. Stainless steel cut wire can produce very bright
surface, but creat much less dust than glass beads, natural and
artificial corundum abrasives. The hardness is 20-40HRC.
Chemical Composition (% by
weight)
|
C |
Si |
Mn |
Ni |
Cr |
others
|
Stainless steel cut wire
(SUS304) |
0.06-0.08 |
1.5-2.0 |
0.9-1.2 |
8.0-10.0 |
16-20 |
|
Conditioned stainless steel cut
wire shot (SUS304) |
0.06-0.08 |
1.5-2.0 |
0.9-1.2 |
8.0-10.0 |
16-20 |
|
Stainless steel cut wire
(SUS430) |
0.1 |
1.2 |
1.0 |
- |
17 |
|
Conditioned stainless steel cut
wire (SUS430) |
0.1 |
1.2 |
1.0 |
- |
17 |
|
Available Sizes
| Material |
stainless steel cut wire shot
(SUS430) |
stainless steel cut wire shot
(SUS304) |
Conditioned stainless steel cut
wire shot (SUS304) |
Size(mm) |
300-450 HV |
400-500 HV |
500 HV |
| 0.2 |
- |
- |
- |
| 0.3 |
v |
v |
v |
| 0.4 |
v |
v |
v |
| 0.5 |
v |
v |
v |
| 0.6 |
v |
v |
v |
| 0.7 |
v |
v |
v |
| 0.8 |
v |
v |
v |
| 1.0 |
v |
v |
v |
| 1.2 |
v |
v |
v |
| 1.5 |
v |
v |
v |
| 2.0 |
v |
v |
v |
| 2.5 |
v |
v |
v |
|
|
| |
|
Aluminium, Zinc & Copper Cut Wires
Zinc cut wire,
Aluminium cut wire and Copper cut wire are made of zinc wire,
aluminium wire and copper wire respectively, widely used for shot
peening to give compressive residual stress in the surface layer of
components for fatigue life enhancement and suppression of stress
corrosion cracking and deburring and cleaning of zinc or aluminum
die cast parts, without any damage to the parts, and creating much
less dust than natural and artificial corundum abrasives. Zinc &
Aluminium cut wire are of reusable and recyclable, have longer work
life than natural and artificial corundum abrasives.
Chemical Content
|
Fe |
Zn |
Al |
Cu |
Cd |
Other
|
Zinc Cut Wire ZN-1 (HV
35-55) |
0.004 |
99.99 |
0.003 |
0.001 |
0.002 |
|
Conditioned Zinc Cut Wire ZN-1 (HV
45-60)
|
0.004 |
99.99 |
0.003 |
0.001 |
0.002 |
|
|
Fe |
Zn |
Al |
Cu |
Mg |
Mn |
Si |
Ti |
Cr |
Other
|
Aluminium Cut Wire
AW1070 (HV 40-60) |
0.16 |
|
99.7 |
0.01 |
|
|
0.16 |
|
|
0.26 |
Aluminium Cut Wire
AW5056 (HV 95-125) |
0.40 |
0.10 |
|
0.10 |
4.5-5.6 |
0.05-0.2 |
0.30 |
0.15 |
0.05-0.2 |
|
|
Fe |
Zn |
P |
Cu+Ag |
Pb |
S |
Ni |
Sn |
Sb |
As
|
other
|
Copper Cut Wire 99
(HV100-150) |
0.004 |
0.003 |
0.002 |
99.95 |
0.004 |
0.004 |
0.002 |
0.002 |
0.002 |
0.002 |
0.053 |
Available Sizes
Zinc Cut Wire ZN-1 (HV
35-55) |
0.8mm, 1.0mm, 1.2mm, 1.5mm, 1.8mm, 2.0mm, 2.5mm |
Conditioned Zinc Cut Wire ZN-1 (HV
45-60)
|
0.6mm, 0.7mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm, 2.5mm |
Aluminium Cut Wire
AW1070 (HV 40-60) |
0.6mm, 0.7mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm, 2.5mm |
Aluminium Cut Wire
AW5056 (HV 95-125) |
0.6mm, 0.7mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm, 2.5mm |
Copper Cut Wire 99
(HV100-150) |
0.6mm, 0.8mm, 1.0mm, 1.5mm, 2.0mm,
2.5mm |
|
|
|
|
|
|
|
|
|
|
|